MAT-7000 measures true density of powders by the liquid
immersion method with high accuracy. It performes automatically weighing,
vacuming of air, pouring of Liquid, calculating the true density and printing
out of measurement results. It can measure up to 4 samples.
One-touch Operation
Model | MAT-7000 |
---|---|
Size | 560(W)×490(H)×470(D)mm |
Weight | 60kg |
Power Source | AC100V 50/60Hz 15A |
Measurement Principle | Pycnometric Technique |
Measurement Time | Within 15 min per sample |
Number Of Samples | 4 samples (continuous measurement) |
Measurable Sample | Powder and granular materials which diameter is 10mm or less and are undissolved in the solvents used. |
Sample | Wait Time | Solvent Temperature | Vacuum Pressure | Vacuuming Time | Solvent | True Density |
---|---|---|---|---|---|---|
Carbon C-1 | 0 | 22.79 | 1 TORR | 10 min | Butanol | 1.7224 g/cc |
Carbon C-2 | 0 | 23.10 | 1 TORR | 10 min | Butanol | 1.7497 g/cc |
NI(1) | 2 | 22.79 | 1 TORR | 15 min | Butanol | 8.2432 g/cc |
Fe-1 | 2 | 23.86 | 1 TORR | 15 min | Butanol | 7.8827 g/cc |
Aluminum | 0 | 20.39 | 7 TORR | 10 min | Etha | 2.7008 g/cc |
Aluminum | 0 | 21.42 | 7 TORR | 10 min | Etha | 2.7003 g/cc |
ZnO | 1 | 29.03 | 7 TORR | 10 min | Butanol | 5.5286 g/cc |
Fe2O3 | 1 | 29.06 | 8 TORR | 10 min | Butanol | 4.5434 g/cc |
CeO2 | 1 | 29.10 | 8 TORR | 10 min | Butanol | 6.0833 g/cc |
SIO2 | 1 | 21.06 | 8 TORR | 10 min | IPA | 2.1989 g/cc |
Y2O3 | 1 | 29.03 | 7 TORR | 10 min | Butanol | 4.6432 g/cc |
Ho2O3 | 1 | 29.51 | 8 TORR | 10 min | Butanol | 7.3131 g/cc |
SnO2 | 1 | 29.16 | 7 TORR | 10 min | Butanol | 6.1805 g/cc |
BiO3 | 1 | 25.68 | 2 TORR | 10 min | Butanol | 8.6510 g/cc |
Mn3O4 | 1 | 25.95 | 2 TORR | 10 min | Butanol | 4.5503 g/cc |