Mainly with dry jet mills as well as cutter mills and?ball mills, from coarse to several μm ultrafine milling and from several to hundreds ton per month, we have various mills to meet a wide range of requirements.
Confition | 1.4 Machine Setting:Operation Condition | Result | ||||||
---|---|---|---|---|---|---|---|---|
Name | Particle Size of Material μm |
Model | Nozzle Pressure | Air Volume | Capacity | Particle Size Distribution | ||
D100 | D50 | kg/cm3 | m3/min | kg/hr | D100 | D50 | ||
Silicon nitride | 20 | 0.75 | FS-4 | 7.0 | 1.0 | 0.67 | 2 | 0.26 |
Silicon nitride | 10 | 0.88 | STJ-200 | 7.0 | 2.6 | 1.7 | 4 | 0.36 |
STJ-200 | 7.0 | 2.6 | 1.7 | 5 | 0.64 | |||
Silicon carbide | 30 | 4.9 | STJ-200 | 7.0 | 2.6 | 0.93 | 3 | 0.35 |
STJ-200 | 7.0 | 2.6 | 0.95 | 2.7 | 0.44 | |||
Silicon carbide | 200mesh | FS-4 | 6.5 | 1.2 | 1 | 15 | 0.43 | |
Silicon | 10 | 1.64 | FS-4 | 7.0 | 1.0 | 0.74 | 10 | 0.49 |
Silicon | 50 | 9.76 | FS-4 | 6.5 | 1.1 | 1.0 | 30 | 6.68 |
Alumina | 48 | 10.0 | FS-4 | 7.0 | 1.0 | 1.0 | 8 | 2.9 |
FS-4 | 7.0 | 1.0 | 0.9 | 8 | 2.7 | |||
Alumina | 130 | 30.0 | FS-4 | 7.0 | 1.1 | 1.0 | 50 | 2.45 |
Barium titanate | 10 | 0.69 | STJ-200 | 6.5~7.0 | 2.6 | 9.5 | 4 | 0.44 |
Zeolite | - | 124.5 | JOM-0202 | 7.0 | 2.6 | 3.8 | 80 | 15 |
JOM-0202 | 7.0 | 2.6 | 10.4 | 80 | 14.2 | |||
Talc powder | 40 | 12.7 | STJ-200 | 7.0 | 2.6 | 1.5 | 10 | 3.52 |
STJ-200 | 7.0 | 2.6 | 4.3 | 10 | 2.97 | |||
Activated carbon | 80 | 14.6 | JOM-0202 | 7.0 | 2.6 | 1.1 | 20 | 5.5 |
JOM-0202 | 7.0 | 2.6 | 4.4 | 20 | 5.7 | |||
Coke | 50 | 12.3 | STJ-200 | 7.0 | 2.6 | 3.9 | 20 | 5.68 |
STJ-200 | 7.0 | 2.6 | 4.5 | 20 | 3.17 | |||
Silica sand | 35 | 6.62 | STJ-200 | 6.5 | 2.6 | 1.49 | 10 | 1.53 |
STJ-200 | 6.5 | 2.6 | 4.78 | 10 | 1.14 | |||
Pigment | 96 | 24.8 | JOM-0202 | 7.0 | 2.6 | 1.16 | 48 | 2.2 |
96 | 24.8 | JOM-0202 | 7.0 | 2.6 | 2.73 | 12 | 1.9 | |
96 | 24.8 | JOM-0202 | 7.0 | 2.6 | 5.0 | 96 | 2.5 | |
Organic pigment(blue) | 20 | 1.4 | JOM-0202 | 7.0 | 2.6 | 1.45 | 10 | 0.3 |
JOM-0202 | 7.0 | 2.6 | 5.9 | 10 | 0.75 |